Kinetika Reaksi Curing Resin Epoksi Dengan Heksametilendiamin = Kinetics of Curing Reaction of Epoxy Resin with Hexamethylenediantine

• 主要作者: Perpustakaan UGM, i-lib
• 格式: Article NonPeerReviewed
• 出版: [Yogyakarta] : Universitas Gadjah Mada 2004
• 主題: Jurnal i-lib UGM
• 在線閱讀: https://repository.ugm.ac.id/23550/; http://i-lib.ugm.ac.id/jurnal/download.php?dataId=6501

Curing reaction of diglycidyl ether of -bisphenol A (DGEBA) with hexamethylenediamine (HMDA) is an addition reaction, forming polymer with a three-dimensional networks structure. This research studied the effect of temperature and initial concentration ratio of HMDA:DGEBA upon the rate constants. There were two rate constants: the rate constant of linear reaction (IQ) and rate constant of branch reaction (k2). This research proposed two models: Ideal model ( based on Flory theory ) and Non-ideal model ( considered structure and molecular weight }. Experiment was carried out in a stirred batch reactor equipped with water bath. Sample was taken at certain time to determine the epoxy equivalent left. DGEBA of 60 g was used. The effect of temperature was investigated at concentration ratio of HMDA : DGEBA of 7 phr with temperature range of 30°C-50°C (5°C interval). The effect of concentration ratio HMDA:DGEBA was investigated at constant temperature of 40°C with concentration ratio range of 4 phr -16 phr ( 3 pill. interval ). It was concluded that the Non-ideal model was more appropriate for the curing reaction of DGEBA with HMDA than the Ideal model. Beside that, Non-ideal model could predict the molecular weight distribution. The effect of reaction temperature and initial concentration ratio HMDA : DGEBA upon the-rate constants could be expressed as : k = CAo 2.4551.105 (� `1731 i exp 4749.24 ) T ) CB° ) k = ' 915 exp( 2.5149.1010 (�CA1 8374.75) T ) 2 C where CAD and CB° were initial concentration of HMDA and DGEBA ( mol/L ) The average errors were 7.57% dan 31.99%, respectively. Keywords : Curing reaction, epoxy resins, Non-ideal model