Pengelasan Dissimilar Metal Baja Karbon Rendah ST 37 dan Baja Austenitik SUS 304 (Tahan Karat) Pada Pengelasan SMAW Terhadap Sifat Mekanik.
The welding process is usually performed for joining, similar materials and it is difficult to weld dissimilar metal. This research aims to study dissimilar metal welds between low carbon steel ST 37 and austenitic stainless steel SUS 304. The experiments were carried out using microscopy in combina...
Saved in:
| 主要作者: | |
|---|---|
| 格式: | Article NonPeerReviewed |
| 出版: |
[Yogyakarta] : Universitas Gadjah Mada
2006
|
| 主題: | |
| 在線閱讀: | https://repository.ugm.ac.id/23193/ http://i-lib.ugm.ac.id/jurnal/download.php?dataId=6135 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | The welding process is usually performed for joining, similar materials and it is difficult to weld dissimilar metal. This research aims to study dissimilar metal welds between low carbon steel ST 37 and austenitic stainless steel SUS 304.
The experiments were carried out using microscopy in combination with mechanical property tests such as tensile, impact, hardness, and bending tests. The welding process used was SMAW with current of 60 ampere. Electrode used were E 304 and R 990. Heat input was maintained low to avoid crack or embrittlement.
Results of the research showed that the tensile stress of the weld made from R 990 electrode was 609 Mpa where as the maximum tensile stress of the weld prepare using E 304 electrode was 377 Mpa.
Keywords: dissimilar metal, tensile test, HAZ, impack |
|---|