STUDI PENGARUH UKURAN BUTIR PARTIKEL DAN STRUKTUR KRISTAL TERHADAP SIFAT DIELEKTRIK NANOPARTIKEL COBALT FERRITE (CoFe2O4)
Cobalt Ferrite (CoFe2O4) has been synthesized with various grain size of particle of 4.3 nm, 7.7 nm, 8.7 nm, 9.0 nm and 9.7 nm using coprecipitation methods then the result was pressed with 50.000N of force to be pellet with diameter of 1 2.26 mm. The measurement uses computerized impedan...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Theses and Dissertations NonPeerReviewed |
| Published: |
[Yogyakarta] : Universitas Gadjah Mada
2014
|
| Subjects: | |
| Online Access: | https://repository.ugm.ac.id/130566/ http://etd.ugm.ac.id/index.php?mod=penelitian_detail&sub=PenelitianDetail&act=view&typ=html&buku_id=70991 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Universitas Gadjah Mada |
| Summary: | Cobalt Ferrite (CoFe2O4) has been synthesized with various grain size of particle
of 4.3 nm, 7.7 nm, 8.7 nm, 9.0 nm and 9.7 nm using coprecipitation methods then
the result was pressed with 50.000N of force to be pellet with diameter of 1 2.26
mm. The measurement uses computerized impedance spectroscopy in the range of
frequency 10 kHz to 120 kHz to investigate its dielectric behaviour toward
frequence and grain size changes of CoFe2O4. The result shows that real dielectric
constant, imaginary dielectric constant, and loss dielectric increase and tend to
constant with the increasing of frequency |
|---|