Characterization of an equal channel angular pressed Al-Zn-In alloy
Equal channel angular pressing (ECAP) is a technique that creates a high accumulated strain in metals and results in ultrafine-grained structure. In this study, Al-5Zn-0.02In was processed by ECAP at a room temperature using route Bc through an ECAP die (press angle of Φ = 100° and Ψ = 20°). The sam...
محفوظ في:
| المؤلفون الرئيسيون: | , , , , , |
|---|---|
| التنسيق: | دورية |
| منشور في: |
2018
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84959504033&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/54619 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| الملخص: | Equal channel angular pressing (ECAP) is a technique that creates a high accumulated strain in metals and results in ultrafine-grained structure. In this study, Al-5Zn-0.02In was processed by ECAP at a room temperature using route Bc through an ECAP die (press angle of Φ = 100° and Ψ = 20°). The samples were subjected to ECAP with 1, 2, 3 and 4 passes. The processed specimens were characterized using electron backscatter diffraction (EBSD). The results confirmed the grain refinement of the alloy after ECAP to an average grain size less than 5 μm after 4-pass ECAP. The microhardness test shows that the hardness increased with the number of passes. The hardness of the cross-sectional area of the sample was similar to that tested along the pressing direction. |
|---|