KAJIAN SIFAT KEMAGNETAN PADA NANOPARTIKEL COBALT FERRITE (CoFe2O4) YANG DIENKAPSULASI DENGAN POLYETHYLENE GLYKOL (PEG-4000) DAN SILIKA

• المؤلفون الرئيسيون: , SULANJARI, , Dr. Edi Suharyadi M.Eng
• التنسيق: Theses and Dissertations NonPeerReviewed
• منشور في: [Yogyakarta] : Universitas Gadjah Mada 2014
• الموضوعات: ETD
• الوصول للمادة أونلاين: https://repository.ugm.ac.id/133371/; http://etd.ugm.ac.id/index.php?mod=penelitian_detail&sub=PenelitianDetail&act=view&typ=html&buku_id=74003
• المؤسسة: Universitas Gadjah Mada

Magnetic nanoparticles of Cobalt ferrite (CoFe2O4) have been succesfully encapsulated with various concentration of PEG-4000 and silica which used as materials for encapsulation. CoFe2O4 powder shynthesized by co-presipitation method. X-ray Diffraction (XRD) showed that after PEG-4000 encapsulated appears new phases on CoFe2O4. It was which is antiferromagnetic and which is paramagnetic. Both of phases was decrease sample respons by eksternal field. Encapsulated of silica has showed the new diffraction peaks, (222) and (331). Transmission Electron Microscopy (TEM) analysis showed that encapsulated PEG-4000 and silica given decreasing agglomeration, controlled shape of nanoparticles more spherical and dispersed. Nanoparticle�s size and degree of crystallinity, increased with increasing concentration of silica. Vibrating Sample Magnetometer VSM analysis show that process of encapsulation by PEG-4000 and silica increasing coersivive field, decreasing saturation and remanent magnetization